S32202 Stainless Steel vs. EN 1.4335 Stainless Steel

Both S32202 stainless steel and EN 1.4335 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S32202 stainless steel and the bottom bar is EN 1.4335 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
45
Fatigue Strength, MPa 400
210
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 79
79
Shear Strength, MPa 490
400
Tensile Strength: Ultimate (UTS), MPa 730
570
Tensile Strength: Yield (Proof), MPa 510
230

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 440
450
Maximum Temperature: Mechanical, °C 1030
1100
Melting Completion (Liquidus), °C 1430
1410
Melting Onset (Solidus), °C 1380
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.6
4.4
Embodied Energy, MJ/kg 37
62
Embodied Water, L/kg 150
190

Common Calculations

PREN (Pitting Resistance) 27
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
210
Resilience: Unit (Modulus of Resilience), kJ/m3 650
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
20
Strength to Weight: Bending, points 24
19
Thermal Diffusivity, mm2/s 4.0
3.7
Thermal Shock Resistance, points 20
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.020
Chromium (Cr), % 21.5 to 24
24 to 26
Iron (Fe), % 69.4 to 77.3
49.4 to 56
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.45
0 to 0.2
Nickel (Ni), % 1.0 to 2.8
20 to 22
Nitrogen (N), % 0.18 to 0.26
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.25
Sulfur (S), % 0 to 0.010
0 to 0.010