UNS S32202 Stainless Steel

S32202 stainless steel is a duplex stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the annealed condition.

It has a fairly low embodied energy among wrought duplex stainless steels. In addition, it has a moderately low base cost and a moderately high ductility.

The graph bars on the material properties cards below compare S32202 stainless steel to: wrought duplex stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

250

Elastic (Young's, Tensile) Modulus

200 GPa 29 x 106 psi

Elongation at Break

34 %

Fatigue Strength

400 MPa 59 x 103 psi

Poisson's Ratio

0.27

Rockwell C Hardness

27

Shear Modulus

79 GPa 11 x 106 psi

Shear Strength

490 MPa 71 x 103 psi

Tensile Strength: Ultimate (UTS)

730 MPa 110 x 103 psi

Tensile Strength: Yield (Proof)

510 MPa 74 x 103 psi

Thermal Properties

Latent Heat of Fusion

290 J/g

Maximum Temperature: Corrosion

440 °C 820 °F

Maximum Temperature: Mechanical

1030 °C 1890 °F

Melting Completion (Liquidus)

1430 °C 2600 °F

Melting Onset (Solidus)

1380 °C 2520 °F

Specific Heat Capacity

480 J/kg-K 0.12 BTU/lb-°F

Thermal Conductivity

15 W/m-K 8.7 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

2.1 % IACS

Electrical Conductivity: Equal Weight (Specific)

2.4 % IACS

Otherwise Unclassified Properties

Base Metal Price

12 % relative

Density

7.7 g/cm3 480 lb/ft3

Embodied Carbon

2.6 kg CO2/kg material

Embodied Energy

37 MJ/kg 16 x 103 BTU/lb

Embodied Water

150 L/kg 18 gal/lb

Common Calculations

PREN (Pitting Resistance)

27

Resilience: Ultimate (Unit Rupture Work)

220 MJ/m3

Resilience: Unit (Modulus of Resilience)

650 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

27 points

Strength to Weight: Bending

24 points

Thermal Diffusivity

4.0 mm2/s

Thermal Shock Resistance

20 points

Alloy Composition

Among wrought stainless steels, the composition of S32202 stainless steel is notable for containing a comparatively high amount of chromium (Cr). Chromium is the defining alloying element of stainless steel. Higher chromium content imparts additional corrosion resistance.

Iron (Fe)Fe 69.4 to 77.3
Chromium (Cr)Cr 21.5 to 24
Nickel (Ni)Ni 1.0 to 2.8
Manganese (Mn)Mn 0 to 2.0
Silicon (Si)Si 0 to 1.0
Molybdenum (Mo)Mo 0 to 0.45
Nitrogen (N)N 0.18 to 0.26
Phosphorus (P)P 0 to 0.040
Carbon (C)C 0 to 0.030
Sulfur (S)S 0 to 0.010

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

Duplex Stainless Steels, Iris Alvarez-Armas and Suzanne Degallaix-Moreuil (editors), 2009

Duplex Stainless Steels: Microstructure, Properties and Applications, Robert N. Gunn (editor), 1997

ASTM A182: Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges, Forged Fittings, and Valves and Parts for High-Temperature Service

ASTM A240: Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications

Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005

Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011

Corrosion of Stainless Steels, A. John Sedriks, 1996

ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994

Advances in Stainless Steels, Baldev Raj et al. (editors), 2010

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015