S35000 Stainless Steel vs. 85-silver 15-nickel
S35000 stainless steel belongs to the iron alloys classification, while 85-silver 15-nickel belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is S35000 stainless steel and the bottom bar is 85-silver 15-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 88 |
| Poisson's Ratio | 0.28 | |
| 0.36 |
| Shear Modulus, GPa | 78 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 1300 to 1570 | |
| 260 to 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 140 |
| Melting Completion (Liquidus), °C | 1460 | |
| 870 |
| Melting Onset (Solidus), °C | 1410 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 86 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 75 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 4.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 14 |
| Strength to Weight: Axial, points | 46 to 56 | |
| 7.1 to 13 |
| Strength to Weight: Bending, points | 34 to 38 | |
| 8.9 to 13 |
| Thermal Shock Resistance, points | 42 to 51 | |
| 12 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0.070 to 0.11 | |
| 0 |
| Chromium (Cr), % | 16 to 17 | |
| 0 |
| Iron (Fe), % | 72.7 to 76.9 | |
| 0 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.2 | |
| 0 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 13.8 to 16 |
| Nitrogen (N), % | 0.070 to 0.13 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 84 to 86 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |