S35000 Stainless Steel vs. EN 1.4539 Stainless Steel

Both S35000 stainless steel and EN 1.4539 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is S35000 stainless steel and the bottom bar is EN 1.4539 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 2.3 to 14
38
Fatigue Strength, MPa 380 to 520
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
79
Shear Strength, MPa 740 to 950
430
Tensile Strength: Ultimate (UTS), MPa 1300 to 1570
630
Tensile Strength: Yield (Proof), MPa 660 to 1160
260

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 410
420
Maximum Temperature: Mechanical, °C 900
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 14
31
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.2
5.7
Embodied Energy, MJ/kg 44
78
Embodied Water, L/kg 130
200

Common Calculations

PREN (Pitting Resistance) 28
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 28 to 170
190
Resilience: Unit (Modulus of Resilience), kJ/m3 1070 to 3360
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 46 to 56
22
Strength to Weight: Bending, points 34 to 38
20
Thermal Diffusivity, mm2/s 4.4
3.2
Thermal Shock Resistance, points 42 to 51
14

Alloy Composition

Carbon (C), % 0.070 to 0.11
0 to 0.020
Chromium (Cr), % 16 to 17
19 to 21
Copper (Cu), % 0
1.2 to 2.0
Iron (Fe), % 72.7 to 76.9
43.1 to 51.8
Manganese (Mn), % 0.5 to 1.3
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.2
4.0 to 5.0
Nickel (Ni), % 4.0 to 5.0
24 to 26
Nitrogen (N), % 0.070 to 0.13
0 to 0.15
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010