S35000 Stainless Steel vs. EN 2.4680 Cast Nickel
S35000 stainless steel belongs to the iron alloys classification, while EN 2.4680 cast nickel belongs to the nickel alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is S35000 stainless steel and the bottom bar is EN 2.4680 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 2.3 to 14 | |
| 9.1 |
| Fatigue Strength, MPa | 380 to 520 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 78 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 1300 to 1570 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 660 to 1160 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 1050 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1410 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 14 |
| Thermal Expansion, µm/m-K | 11 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 60 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 9.1 |
| Embodied Energy, MJ/kg | 44 | |
| 130 |
| Embodied Water, L/kg | 130 | |
| 350 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 to 170 | |
| 45 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1070 to 3360 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 46 to 56 | |
| 21 |
| Strength to Weight: Bending, points | 34 to 38 | |
| 20 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 3.7 |
| Thermal Shock Resistance, points | 42 to 51 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0.070 to 0.11 | |
| 0 to 0.1 |
| Chromium (Cr), % | 16 to 17 | |
| 48 to 52 |
| Iron (Fe), % | 72.7 to 76.9 | |
| 0 to 1.0 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 2.5 to 3.2 | |
| 0 to 0.5 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 42.9 to 51 |
| Niobium (Nb), % | 0 | |
| 1.0 to 1.8 |
| Nitrogen (N), % | 0.070 to 0.13 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |