S41050 Stainless Steel vs. EN 1.4021 Stainless Steel

Both S41050 stainless steel and EN 1.4021 stainless steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is S41050 stainless steel and the bottom bar is EN 1.4021 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 25
11 to 17
Fatigue Strength, MPa 160
240 to 380
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 300
390 to 530
Tensile Strength: Ultimate (UTS), MPa 470
630 to 880
Tensile Strength: Yield (Proof), MPa 230
390 to 670

Thermal Properties

Latent Heat of Fusion, J/g 270
270
Maximum Temperature: Corrosion, °C 390
390
Maximum Temperature: Mechanical, °C 720
760
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
30
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
7.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.9
1.9
Embodied Energy, MJ/kg 27
27
Embodied Water, L/kg 97
100

Common Calculations

PREN (Pitting Resistance) 12
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 98
88 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
400 to 1160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
23 to 31
Strength to Weight: Bending, points 17
21 to 26
Thermal Diffusivity, mm2/s 7.2
8.1
Thermal Shock Resistance, points 17
22 to 31

Alloy Composition

Carbon (C), % 0 to 0.040
0.16 to 0.25
Chromium (Cr), % 10.5 to 12.5
12 to 14
Iron (Fe), % 84.2 to 88.9
83.2 to 87.8
Manganese (Mn), % 0 to 1.0
0 to 1.5
Nickel (Ni), % 0.6 to 1.1
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015