S45000 Stainless Steel vs. EN 1.3542 Stainless Steel

Both S45000 stainless steel and EN 1.3542 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is S45000 stainless steel and the bottom bar is EN 1.3542 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 280 to 410
220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 980 to 1410
720

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Corrosion, °C 400
380
Maximum Temperature: Mechanical, °C 840
770
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
29
Thermal Expansion, µm/m-K 11
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.6

Otherwise Unclassified Properties

Base Metal Price, % relative 13
7.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.0
Embodied Energy, MJ/kg 39
29
Embodied Water, L/kg 130
100

Common Calculations

PREN (Pitting Resistance) 17
15
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 35 to 50
26
Strength to Weight: Bending, points 28 to 36
23
Thermal Diffusivity, mm2/s 4.5
7.9
Thermal Shock Resistance, points 33 to 47
26

Alloy Composition

Carbon (C), % 0 to 0.050
0.6 to 0.7
Chromium (Cr), % 14 to 16
12.5 to 14.5
Copper (Cu), % 1.3 to 1.8
0
Iron (Fe), % 72.1 to 79.3
82.7 to 87.5
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.5 to 1.0
0 to 0.75
Nickel (Ni), % 5.0 to 7.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030