S45000 Stainless Steel vs. SAE-AISI M43 Steel

Both S45000 stainless steel and SAE-AISI M43 steel are iron alloys. They have 79% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is S45000 stainless steel and the bottom bar is SAE-AISI M43 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 980 to 1410
810 to 2290

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1440
1550
Melting Onset (Solidus), °C 1390
1500
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 17
19
Thermal Expansion, µm/m-K 11
12

Otherwise Unclassified Properties

Base Metal Price, % relative 13
33
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 2.8
8.5
Embodied Energy, MJ/kg 39
120
Embodied Water, L/kg 130
140

Common Calculations

PREN (Pitting Resistance) 17
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 35 to 50
27 to 77
Strength to Weight: Bending, points 28 to 36
24 to 47
Thermal Diffusivity, mm2/s 4.5
5.3
Thermal Shock Resistance, points 33 to 47
25 to 71

Alloy Composition

Carbon (C), % 0 to 0.050
1.2 to 1.3
Chromium (Cr), % 14 to 16
3.5 to 4.3
Cobalt (Co), % 0
7.8 to 8.8
Copper (Cu), % 1.3 to 1.8
0 to 0.25
Iron (Fe), % 72.1 to 79.3
70.8 to 76
Manganese (Mn), % 0 to 1.0
0.2 to 0.4
Molybdenum (Mo), % 0.5 to 1.0
7.5 to 8.5
Nickel (Ni), % 5.0 to 7.0
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.15 to 0.65
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
2.3 to 3.0
Vanadium (V), % 0
1.5 to 1.8

Comparable Variants