S45000 Stainless Steel vs. SAE-AISI S4 Steel

Both S45000 stainless steel and SAE-AISI S4 steel are iron alloys. They have 77% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S45000 stainless steel and the bottom bar is SAE-AISI S4 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 980 to 1410
670 to 2140

Thermal Properties

Latent Heat of Fusion, J/g 280
280
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
44
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.2
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.0
Embodied Energy, MJ/kg 39
29
Embodied Water, L/kg 130
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 35 to 50
24 to 77
Strength to Weight: Bending, points 28 to 36
22 to 48
Thermal Diffusivity, mm2/s 4.5
12
Thermal Shock Resistance, points 33 to 47
20 to 65

Alloy Composition

Carbon (C), % 0 to 0.050
0.5 to 0.65
Chromium (Cr), % 14 to 16
0.1 to 0.5
Copper (Cu), % 1.3 to 1.8
0
Iron (Fe), % 72.1 to 79.3
95.2 to 96.9
Manganese (Mn), % 0 to 1.0
0.6 to 1.0
Molybdenum (Mo), % 0.5 to 1.0
0
Nickel (Ni), % 5.0 to 7.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
1.8 to 2.3
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0
0.15 to 0.35

Comparable Variants