S45503 Stainless Steel vs. AISI 201LN Stainless Steel
Both S45503 stainless steel and AISI 201LN stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is S45503 stainless steel and the bottom bar is AISI 201LN stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 410 to 500 | |
| 210 to 320 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 4.6 to 6.8 | |
| 25 to 51 |
| Fatigue Strength, MPa | 710 to 800 | |
| 340 to 540 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Shear Strength, MPa | 940 to 1070 | |
| 530 to 680 |
| Tensile Strength: Ultimate (UTS), MPa | 1610 to 1850 | |
| 740 to 1060 |
| Tensile Strength: Yield (Proof), MPa | 1430 to 1700 | |
| 350 to 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 640 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 880 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1410 |
| Melting Onset (Solidus), °C | 1400 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 12 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 48 | |
| 38 |
| Embodied Water, L/kg | 120 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 110 | |
| 230 to 310 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 57 to 65 | |
| 27 to 38 |
| Strength to Weight: Bending, points | 39 to 43 | |
| 24 to 30 |
| Thermal Shock Resistance, points | 56 to 64 | |
| 16 to 23 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0 to 0.030 |
| Chromium (Cr), % | 11 to 12.5 | |
| 16 to 17.5 |
| Copper (Cu), % | 1.5 to 2.5 | |
| 0 to 1.0 |
| Iron (Fe), % | 72.4 to 78.9 | |
| 67.9 to 73.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 6.4 to 7.5 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 7.5 to 9.5 | |
| 4.0 to 5.0 |
| Niobium (Nb), % | 0.1 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.25 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.015 |
| Titanium (Ti), % | 1.0 to 1.4 | |
| 0 |