S45503 Stainless Steel vs. K93600 Alloy
Both S45503 stainless steel and K93600 alloy are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is S45503 stainless steel and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
140 |
Elongation at Break, % | 4.6 to 6.8 | |
5.0 to 35 |
Shear Strength, MPa | 940 to 1070 | |
320 to 380 |
Tensile Strength: Ultimate (UTS), MPa | 1610 to 1850 | |
480 to 810 |
Tensile Strength: Yield (Proof), MPa | 1430 to 1700 | |
280 to 750 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 760 | |
440 |
Melting Onset (Solidus), °C | 1400 | |
1430 |
Specific Heat Capacity, J/kg-K | 470 | |
520 |
Thermal Expansion, µm/m-K | 11 | |
7.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.9 | |
8.1 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 110 | |
21 to 280 |
Stiffness to Weight: Axial, points | 14 | |
9.4 |
Stiffness to Weight: Bending, points | 24 | |
21 |
Strength to Weight: Axial, points | 57 to 65 | |
16 to 28 |
Strength to Weight: Bending, points | 39 to 43 | |
17 to 24 |
Thermal Shock Resistance, points | 56 to 64 | |
34 to 57 |