S46500 Stainless Steel vs. K93600 Alloy
Both S46500 stainless steel and K93600 alloy are iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is S46500 stainless steel and the bottom bar is K93600 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 2.3 to 14 | |
| 5.0 to 35 |
| Shear Strength, MPa | 730 to 1120 | |
| 320 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 1260 to 1930 | |
| 480 to 810 |
| Tensile Strength: Yield (Proof), MPa | 1120 to 1810 | |
| 280 to 750 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 780 | |
| 440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 520 |
| Thermal Expansion, µm/m-K | 11 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.1 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 210 | |
| 21 to 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 9.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 44 to 68 | |
| 16 to 28 |
| Strength to Weight: Bending, points | 33 to 44 | |
| 17 to 24 |
| Thermal Shock Resistance, points | 44 to 67 | |
| 34 to 57 |