Work Hardened 92-silver 8-tin-oxide vs. Work Hardened ASTM B522 Class I
Both work hardened 92-silver 8-tin-oxide and work hardened ASTM B522 class I are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 6 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is work hardened 92-silver 8-tin-oxide and the bottom bar is work hardened ASTM B522 class I.
Metric UnitsUS Customary Units
Material Properties
Electrical Conductivity: Equal Volume, % IACS | 76 | |
11 |
Elongation at Break, % | 34 | |
1.1 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
4.5 |
Shear Strength, MPa | 210 | |
280 |
Tensile Strength: Ultimate (UTS), MPa | 320 | |
490 |
Tensile Strength: Yield (Proof), MPa | 300 | |
210 |