ZK40A Magnesium vs. SAE-AISI 1095 Steel

ZK40A magnesium belongs to the magnesium alloys classification, while SAE-AISI 1095 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZK40A magnesium and the bottom bar is SAE-AISI 1095 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 4.2
10 to 11
Fatigue Strength, MPa 190
310 to 370
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
72
Shear Strength, MPa 160
400 to 540
Tensile Strength: Ultimate (UTS), MPa 280
680 to 900
Tensile Strength: Yield (Proof), MPa 260
500 to 590

Thermal Properties

Latent Heat of Fusion, J/g 340
240
Maximum Temperature: Mechanical, °C 120
400
Melting Completion (Liquidus), °C 600
1450
Melting Onset (Solidus), °C 540
1410
Specific Heat Capacity, J/kg-K 970
470
Thermal Conductivity, W/m-K 110
47
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
9.6
Electrical Conductivity: Equal Weight (Specific), % IACS 130
11

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.8
Density, g/cm3 1.8
7.8
Embodied Carbon, kg CO2/kg material 24
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 950
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12
63 to 84
Resilience: Unit (Modulus of Resilience), kJ/m3 740
660 to 930
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 65
24
Strength to Weight: Axial, points 43
24 to 32
Strength to Weight: Bending, points 53
22 to 26
Thermal Diffusivity, mm2/s 62
13
Thermal Shock Resistance, points 17
22 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0
0.9 to 1.0
Iron (Fe), % 0
98.4 to 98.8
Magnesium (Mg), % 94.2 to 96.1
0
Manganese (Mn), % 0
0.3 to 0.5
Phosphorus (P), % 0
0 to 0.040
Sulfur (S), % 0
0 to 0.050
Zinc (Zn), % 3.5 to 4.5
0
Zirconium (Zr), % 0.45 to 1.0
0
Residuals, % 0 to 0.3
0