ZK40A Magnesium vs. C87200 Bronze

ZK40A magnesium belongs to the magnesium alloys classification, while C87200 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ZK40A magnesium and the bottom bar is C87200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
110
Elongation at Break, % 4.2
30
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Tensile Strength: Ultimate (UTS), MPa 280
380
Tensile Strength: Yield (Proof), MPa 260
170

Thermal Properties

Latent Heat of Fusion, J/g 340
260
Maximum Temperature: Mechanical, °C 120
200
Melting Completion (Liquidus), °C 600
970
Melting Onset (Solidus), °C 540
860
Specific Heat Capacity, J/kg-K 970
410
Thermal Conductivity, W/m-K 110
28
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 130
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 13
29
Density, g/cm3 1.8
8.6
Embodied Carbon, kg CO2/kg material 24
2.7
Embodied Energy, MJ/kg 160
44
Embodied Water, L/kg 950
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 12
93
Resilience: Unit (Modulus of Resilience), kJ/m3 740
130
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 65
19
Strength to Weight: Axial, points 43
12
Strength to Weight: Bending, points 53
14
Thermal Diffusivity, mm2/s 62
8.0
Thermal Shock Resistance, points 17
14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0 to 1.5
Copper (Cu), % 0
89 to 99
Iron (Fe), % 0
0 to 2.5
Lead (Pb), % 0
0 to 0.5
Magnesium (Mg), % 94.2 to 96.1
0
Manganese (Mn), % 0
0 to 1.5
Phosphorus (P), % 0
0 to 0.5
Silicon (Si), % 0
1.0 to 5.0
Tin (Sn), % 0
0 to 1.0
Zinc (Zn), % 3.5 to 4.5
0 to 5.0
Zirconium (Zr), % 0.45 to 1.0
0
Residuals, % 0 to 0.3
0