Zamak 5 vs. EN 1.4912 Stainless Steel

Zamak 5 belongs to the zinc alloys classification, while EN 1.4912 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is Zamak 5 and the bottom bar is EN 1.4912 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92
180
Elastic (Young's, Tensile) Modulus, GPa 87
200
Elongation at Break, % 6.3
40
Fatigue Strength, MPa 56
200
Poisson's Ratio 0.25
0.28
Shear Modulus, GPa 33
77
Shear Strength, MPa 260
420
Tensile Strength: Ultimate (UTS), MPa 330
610
Tensile Strength: Yield (Proof), MPa 240
230

Thermal Properties

Latent Heat of Fusion, J/g 120
290
Maximum Temperature: Mechanical, °C 95
940
Melting Completion (Liquidus), °C 390
1430
Melting Onset (Solidus), °C 380
1390
Specific Heat Capacity, J/kg-K 410
480
Thermal Conductivity, W/m-K 110
16
Thermal Expansion, µm/m-K 27
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 37
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 12
20
Density, g/cm3 6.4
7.8
Embodied Carbon, kg CO2/kg material 3.0
3.8
Embodied Energy, MJ/kg 57
55
Embodied Water, L/kg 380
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19
190
Resilience: Unit (Modulus of Resilience), kJ/m3 330
130
Stiffness to Weight: Axial, points 7.5
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 14
22
Strength to Weight: Bending, points 16
20
Thermal Diffusivity, mm2/s 42
4.2
Thermal Shock Resistance, points 9.9
14

Alloy Composition

Aluminum (Al), % 3.5 to 4.3
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.040 to 0.1
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0.7 to 1.3
0
Iron (Fe), % 0 to 0.1
64.6 to 73.6
Lead (Pb), % 0 to 0.0050
0
Magnesium (Mg), % 0.025 to 0.080
0
Manganese (Mn), % 0
0 to 2.0
Nickel (Ni), % 0 to 0.020
9.0 to 12
Niobium (Nb), % 0
0.4 to 1.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.030
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.0030
0
Zinc (Zn), % 94.3 to 95.7
0