ZA-8 vs. C52400 Bronze
ZA-8 belongs to the zinc alloys classification, while C52400 bronze belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is ZA-8 and the bottom bar is C52400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 85 to 86 | |
| 110 |
| Poisson's Ratio | 0.26 | |
| 0.34 |
| Rockwell B Hardness | 54 to 65 | |
| 50 to 100 |
| Shear Modulus, GPa | 34 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 210 to 370 | |
| 450 to 880 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 100 | |
| 170 |
| Melting Completion (Liquidus), °C | 400 | |
| 1000 |
| Melting Onset (Solidus), °C | 380 | |
| 840 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 370 |
| Thermal Conductivity, W/m-K | 120 | |
| 50 |
| Thermal Expansion, µm/m-K | 23 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 28 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 40 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 35 |
| Density, g/cm3 | 6.3 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 3.6 |
| Embodied Energy, MJ/kg | 62 | |
| 58 |
| Embodied Water, L/kg | 420 | |
| 390 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.5 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 9.3 to 17 | |
| 14 to 28 |
| Strength to Weight: Bending, points | 12 to 18 | |
| 15 to 23 |
| Thermal Diffusivity, mm2/s | 42 | |
| 15 |
| Thermal Shock Resistance, points | 7.6 to 13 | |
| 17 to 32 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 8.0 to 8.8 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0060 | |
| 0 |
| Copper (Cu), % | 0.8 to 1.3 | |
| 87.8 to 91 |
| Iron (Fe), % | 0 to 0.075 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.0060 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.015 to 0.030 | |
| 0 |
| Nickel (Ni), % | 0 to 0.020 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.030 to 0.35 |
| Silicon (Si), % | 0 to 0.045 | |
| 0 |
| Tin (Sn), % | 0 to 0.0030 | |
| 9.0 to 11 |
| Zinc (Zn), % | 89.7 to 91.2 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.5 |