Z41321 Zinc vs. EN 1.0259 Steel

Z41321 zinc belongs to the zinc alloys classification, while EN 1.0259 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is Z41321 zinc and the bottom bar is EN 1.0259 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 87
190
Elongation at Break, % 60
23
Poisson's Ratio 0.25
0.29
Shear Modulus, GPa 35
73
Tensile Strength: Ultimate (UTS), MPa 190
490
Tensile Strength: Yield (Proof), MPa 150
280

Thermal Properties

Latent Heat of Fusion, J/g 110
250
Maximum Temperature: Mechanical, °C 90
400
Melting Completion (Liquidus), °C 410
1460
Melting Onset (Solidus), °C 400
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 110
49
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 37
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 6.6
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.5
Embodied Energy, MJ/kg 54
19
Embodied Water, L/kg 340
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
95
Resilience: Unit (Modulus of Resilience), kJ/m3 130
210
Stiffness to Weight: Axial, points 7.4
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 7.9
17
Strength to Weight: Bending, points 11
18
Thermal Diffusivity, mm2/s 44
13
Thermal Shock Resistance, points 5.9
15

Alloy Composition

Aluminum (Al), % 0 to 0.010
0.020 to 0.2
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.2
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0.5 to 1.0
0 to 0.3
Iron (Fe), % 0 to 0.010
96.7 to 99.98
Lead (Pb), % 0 to 0.010
0
Manganese (Mn), % 0
0 to 1.4
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 0 to 0.0030
0
Titanium (Ti), % 0.080 to 0.18
0 to 0.040
Vanadium (V), % 0
0 to 0.020
Zinc (Zn), % 98.8 to 99.42
0