333.0-T5 Cast Aluminum
333.0-T5 aluminum is 333.0 aluminum in the T5 temper. To achieve this temper, the metal is artificially aged until it meets standard mechanical property requirements. It has the lowest ductility compared to the other variants of 333.0 aluminum.
The graph bars on the material properties cards below compare 333.0-T5 aluminum to: ANSI/AA cast aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
100
Elastic (Young's, Tensile) Modulus
73 GPa 11 x 106 psi
Elongation at Break
1.0 %
Fatigue Strength
83 MPa 12 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
28 GPa 4.0 x 106 psi
Shear Strength
190 MPa 27 x 103 psi
Tensile Strength: Ultimate (UTS)
230 MPa 34 x 103 psi
Tensile Strength: Yield (Proof)
170 MPa 25 x 103 psi
Thermal Properties
Latent Heat of Fusion
520 J/g
Maximum Temperature: Mechanical
170 °C 340 °F
Melting Completion (Liquidus)
590 °C 1090 °F
Melting Onset (Solidus)
530 °C 990 °F
Specific Heat Capacity
880 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
120 W/m-K 70 BTU/h-ft-°F
Thermal Expansion
21 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
29 % IACS
Electrical Conductivity: Equal Weight (Specific)
92 % IACS
Otherwise Unclassified Properties
Base Metal Price
10 % relative
Density
2.8 g/cm3 180 lb/ft3
Embodied Carbon
7.6 kg CO2/kg material
Embodied Energy
140 MJ/kg 61 x 103 BTU/lb
Embodied Water
1040 L/kg 120 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
2.1 MJ/m3
Resilience: Unit (Modulus of Resilience)
200 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
49 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
30 points
Thermal Diffusivity
49 mm2/s
Thermal Shock Resistance
11 points
Alloy Composition
| Al | 81.8 to 89 | |
| Si | 8.0 to 10 | |
| Cu | 3.0 to 4.0 | |
| Fe | 0 to 1.0 | |
| Zn | 0 to 1.0 | |
| Mg | 0.050 to 0.5 | |
| Mn | 0 to 0.5 | |
| Ni | 0 to 0.5 | |
| Ti | 0 to 0.25 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings
Iron in Aluminium Alloys: Impurity and Alloying Element, N. A. Belov et al., 2002
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015