ASTM A209 Grade T1 C-Mo Steel
ASTM A209 grade T1 is a type of ASTM A209 steel. Cited properties are appropriate for the normalized condition. The graph bars on the material properties cards below compare ASTM A209 grade T1 to: wrought alloy steels in the same category (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
150
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
34 %
Fatigue Strength
180 MPa 27 x 103 psi
Poisson's Ratio
0.29
Rockwell B Hardness
80
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
290 MPa 42 x 103 psi
Tensile Strength: Ultimate (UTS)
430 MPa 63 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
410 °C 760 °F
Melting Completion (Liquidus)
1470 °C 2670 °F
Melting Onset (Solidus)
1420 °C 2600 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
50 W/m-K 29 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.2 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.4 % relative
Density
7.9 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
20 MJ/kg 8.6 x 103 BTU/lb
Embodied Water
47 L/kg 5.6 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
140 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
15 points
Strength to Weight: Bending
16 points
Thermal Diffusivity
13 mm2/s
Thermal Shock Resistance
13 points
Alloy Composition
| Fe | 97.8 to 99.06 | |
| Mn | 0.3 to 0.8 | |
| Mo | 0.44 to 0.65 | |
| Si | 0.1 to 0.5 | |
| C | 0.1 to 0.2 | |
| P | 0 to 0.025 | |
| S | 0 to 0.025 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
ASTM A209: Standard Specification for Seamless Carbon-Molybdenum Alloy-Steel Boiler and Superheater Tubes
Pressure Vessels: External Pressure Technology, 2nd ed., Carl T. F. Ross, 2011
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015