Annealed (+A) 1.4006 Stainless Steel
EN 1.4006 +A steel is EN 1.4006 stainless steel in the annealed condition. It has the lowest strength and highest ductility compared to the other variants of EN 1.4006 stainless steel. The graph bars on the material properties cards below compare EN 1.4006 +A steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
190
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
23 %
Fatigue Strength
150 MPa 22 x 103 psi
Poisson's Ratio
0.28
Rockwell B Hardness
77
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
370 MPa 54 x 103 psi
Tensile Strength: Ultimate (UTS)
590 MPa 85 x 103 psi
Tensile Strength: Yield (Proof)
230 MPa 33 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
740 °C 1370 °F
Melting Completion (Liquidus)
1440 °C 2630 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.9 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.3 % IACS
Otherwise Unclassified Properties
Base Metal Price
7.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
1.9 kg CO2/kg material
Embodied Energy
27 MJ/kg 12 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
13
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
140 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
20 points
Thermal Diffusivity
8.1 mm2/s
Thermal Shock Resistance
21 points
Alloy Composition
| Fe | 83.1 to 88.4 | |
| Cr | 11.5 to 13.5 | |
| Mn | 0 to 1.5 | |
| Si | 0 to 1.0 | |
| Ni | 0 to 0.75 | |
| C | 0.080 to 0.15 | |
| P | 0 to 0.040 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10272: Stainless steel bars for pressure purposes
EN 10250-4: Open die steel forgings for general engineering purposes - Part 4: Stainless steels
EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010