EN 1.4828 (X15CrNiSi20-12) Stainless Steel
EN 1.4828 stainless steel is an austenitic stainless steel formulated for primary forming into wrought products. Cited properties are appropriate for the solution annealed (AT) condition. 1.4828 is the EN numeric designation for this material. X15CrNiSi20-12 is the EN chemical designation.
It has a moderately low electrical conductivity and a fairly low ductility among wrought austenitic stainless steels.
The graph bars on the material properties cards below compare EN 1.4828 stainless steel to: wrought austenitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
190
Elastic (Young's, Tensile) Modulus
200 GPa 28 x 106 psi
Elongation at Break
33 %
Fatigue Strength
200 MPa 29 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
77 GPa 11 x 106 psi
Shear Strength
430 MPa 63 x 103 psi
Tensile Strength: Ultimate (UTS)
650 MPa 94 x 103 psi
Tensile Strength: Yield (Proof)
260 MPa 38 x 103 psi
Thermal Properties
Latent Heat of Fusion
320 J/g
Maximum Temperature: Corrosion
420 °C 790 °F
Maximum Temperature: Mechanical
1000 °C 1830 °F
Melting Completion (Liquidus)
1400 °C 2550 °F
Melting Onset (Solidus)
1360 °C 2470 °F
Specific Heat Capacity
490 J/kg-K 0.12 BTU/lb-°F
Thermal Conductivity
15 W/m-K 8.7 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.4 % IACS
Otherwise Unclassified Properties
Base Metal Price
17 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
3.4 kg CO2/kg material
Embodied Energy
48 MJ/kg 21 x 103 BTU/lb
Embodied Water
150 L/kg 18 gal/lb
Common Calculations
PREN (Pitting Resistance)
21
Resilience: Ultimate (Unit Rupture Work)
170 MJ/m3
Resilience: Unit (Modulus of Resilience)
170 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
23 points
Strength to Weight: Bending
22 points
Thermal Diffusivity
4.0 mm2/s
Thermal Shock Resistance
14 points
Alloy Composition
Among wrought stainless steels, the composition of EN 1.4828 stainless steel is notable for containing a comparatively high amount of silicon (Si). Silicon content is typically governed by metallurgical processing concerns, but it can also be added for the purpose of improving oxidation resistance.
| Fe | 61.1 to 68.5 | |
| Cr | 19 to 21 | |
| Ni | 11 to 13 | |
| Si | 1.5 to 2.5 | |
| Mn | 0 to 2.0 | |
| C | 0 to 0.2 | |
| N | 0 to 0.1 | |
| P | 0 to 0.045 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10095: Heat resisting steels and nickel alloys
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Corrosion of Austenitic Stainless Steels: Mechanism, Mitigation and Monitoring, H. S. Khatak and B. Raj (editors), 2002
Austenitic Stainless Steels: Microstructure and Mechanical Properties, P. Marshall, 1984
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010