H1150 Hardened S17400 Stainless Steel
H1150 hardened S17400 stainless steel is S17400 stainless steel in the hardened (H) condition. The graph bars on the material properties cards below compare H1150 hardened S17400 stainless steel to: wrought precipitation-hardening stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
320
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
17 %
Fatigue Strength
470 MPa 68 x 103 psi
Impact Strength: V-Notched Charpy
46 J 34 ft-lb
Poisson's Ratio
0.28
Reduction in Area
57 %
Rockwell C Hardness
30
Shear Modulus
75 GPa 11 x 106 psi
Shear Strength
610 MPa 88 x 103 psi
Tensile Strength: Ultimate (UTS)
990 MPa 140 x 103 psi
Tensile Strength: Yield (Proof)
780 MPa 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
280 J/g
Maximum Temperature: Corrosion
450 °C 840 °F
Maximum Temperature: Mechanical
850 °C 1570 °F
Melting Completion (Liquidus)
1440 °C 2620 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
17 W/m-K 9.7 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
2.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
14 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
39 MJ/kg 17 x 103 BTU/lb
Embodied Water
130 L/kg 16 gal/lb
Common Calculations
PREN (Pitting Resistance)
16
Resilience: Ultimate (Unit Rupture Work)
160 MJ/m3
Resilience: Unit (Modulus of Resilience)
1560 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
35 points
Strength to Weight: Bending
28 points
Thermal Diffusivity
4.5 mm2/s
Thermal Shock Resistance
33 points
Alloy Composition
| Fe | 70.4 to 78.9 | |
| Cr | 15 to 17 | |
| Ni | 3.0 to 5.0 | |
| Cu | 3.0 to 5.0 | |
| Mn | 0 to 1.0 | |
| Si | 0 to 1.0 | |
| Nb | 0.15 to 0.45 | |
| C | 0 to 0.070 | |
| P | 0 to 0.040 | |
| S | 0 to 0.030 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM A564: Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
Sintering of Advanced Materials: Fundamentals and Processes, Zhigang Zak Fang (editor), 2010
ASTM A276: Standard Specification for Stainless Steel Bars and Shapes
Welding Metallurgy and Weldability of Stainless Steels, John C. Lippold and Damian J. Kotecki, 2005
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Corrosion of Stainless Steels, A. John Sedriks, 1996
ASM Specialty Handbook: Stainless Steels, J. R. Davis (editor), 1994
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010