MakeItFrom.com
Menu (ESC)

Hardened D2 Tool Steel

Hardened SAE-AISI D2 is SAE-AISI D2 steel in the hardened (H) condition. The graph bars on the material properties cards below compare hardened SAE-AISI D2 to: tool steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Elastic (Young's, Tensile) Modulus

190 GPa 28 x 106 psi

Elongation at Break

5.0 %

Fatigue Strength

860 MPa 120 x 103 psi

Poisson's Ratio

0.28

Rockwell C Hardness

62

Shear Modulus

75 GPa 11 x 106 psi

Shear Strength

1160 MPa 170 x 103 psi

Tensile Strength: Ultimate (UTS)

2000 MPa 290 x 103 psi

Tensile Strength: Yield (Proof)

1510 MPa 220 x 103 psi

Thermal Properties

Latent Heat of Fusion

270 J/g

Melting Completion (Liquidus)

1440 °C 2620 °F

Melting Onset (Solidus)

1390 °C 2540 °F

Specific Heat Capacity

480 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

31 W/m-K 18 BTU/h-ft-°F

Thermal Expansion

11 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

4.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

5.1 % IACS

Otherwise Unclassified Properties

Base Metal Price

8.0 % relative

Density

7.7 g/cm3 480 lb/ft3

Embodied Carbon

3.4 kg CO2/kg material

Embodied Energy

50 MJ/kg 22 x 103 BTU/lb

Embodied Water

100 L/kg 12 gal/lb

Common Calculations

PREN (Pitting Resistance)

15

Resilience: Ultimate (Unit Rupture Work)

92 MJ/m3

Resilience: Unit (Modulus of Resilience)

5940 kJ/m3

Stiffness to Weight: Axial

14 points

Stiffness to Weight: Bending

25 points

Strength to Weight: Axial

72 points

Strength to Weight: Bending

46 points

Thermal Diffusivity

8.3 mm2/s

Thermal Shock Resistance

67 points

Alloy Composition

Iron (Fe)Fe 81.3 to 86.9
Chromium (Cr)Cr 11 to 13
Carbon (C)C 1.4 to 1.6
Molybdenum (Mo)Mo 0.7 to 1.2
Vanadium (V)V 0 to 1.1
Manganese (Mn)Mn 0 to 0.6
Silicon (Si)Si 0 to 0.6
Nickel (Ni)Ni 0 to 0.3
Copper (Cu)Cu 0 to 0.25
Phosphorus (P)P 0 to 0.030
Sulfur (S)S 0 to 0.030

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

SAE J437: Selection and Heat Treatment of Tool and Die Steels

ASTM A681: Standard Specification for Tool Steels Alloy

Tool Steels, 5th ed., George Roberts et al., 1998

Tool Steels: Properties and Performance, Rafael A. Mesquita (editor), 2016

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015