Hot Rolled 1144 Carbon Steel

Hot rolled SAE-AISI 1144 is SAE-AISI 1144 steel in the hot worked condition. The graph bars on the material properties cards below compare hot rolled SAE-AISI 1144 to: wrought resulfurized carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

220

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

17 %

Fatigue Strength

280 MPa 41 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

40 %

Shear Modulus

72 GPa 10 x 106 psi

Shear Strength

460 MPa 67 x 103 psi

Tensile Strength: Ultimate (UTS)

750 MPa 110 x 103 psi

Tensile Strength: Yield (Proof)

420 MPa 61 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1450 °C 2650 °F

Melting Onset (Solidus)

1410 °C 2580 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

51 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

13 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.2 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.2 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.9 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.0 x 103 BTU/lb

Embodied Water

47 L/kg 5.7 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

110 MJ/m3

Resilience: Unit (Modulus of Resilience)

480 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

27 points

Strength to Weight: Bending

23 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

22 points

Alloy Composition

Iron (Fe)Fe 97.5 to 98
Manganese (Mn)Mn 1.4 to 1.7
Carbon (C)C 0.4 to 0.48
Sulfur (S)S 0.24 to 0.33
Phosphorus (P)P 0 to 0.040

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Further Reading

ASTM A29: Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for

Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004

Carbon Steel Handbook, D. Gandy, 2007

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015