SAE-AISI 1022 (G10220) Carbon Steel

SAE-AISI 1022 steel is a carbon (non-alloy) steel formulated for primary forming into wrought products. 1022 is the designation in both the SAE and AISI systems for this material. G10220 is the UNS number.

The properties of SAE-AISI 1022 steel include two common variations. This page shows summary ranges across both of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare SAE-AISI 1022 steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

150 to 160

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

17 to 26 %

Fatigue Strength

190 to 300 MPa 28 to 43 x 103 psi

Poisson's Ratio

0.29

Reduction in Area

45 to 54 %

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

310 to 340 MPa 45 to 49 x 103 psi

Tensile Strength: Ultimate (UTS)

480 to 550 MPa 70 to 79 x 103 psi

Tensile Strength: Yield (Proof)

260 to 450 MPa 38 to 65 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2670 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

52 W/m-K 30 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.0 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.0 % IACS

Otherwise Unclassified Properties

Base Metal Price

1.8 % relative

Density

7.9 g/cm3 490 lb/ft3

Embodied Carbon

1.4 kg CO2/kg material

Embodied Energy

18 MJ/kg 7.9 x 103 BTU/lb

Embodied Water

46 L/kg 5.5 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

88 to 110 MJ/m3

Resilience: Unit (Modulus of Resilience)

190 to 530 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

17 to 19 points

Strength to Weight: Bending

17 to 19 points

Thermal Diffusivity

14 mm2/s

Thermal Shock Resistance

15 to 17 points

Alloy Composition

Iron (Fe)Fe 98.7 to 99.12
Manganese (Mn)Mn 0.7 to 1.0
Carbon (C)C 0.18 to 0.23
Sulfur (S)S 0 to 0.050
Phosphorus (P)P 0 to 0.040

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

Cold-Formed Steel Structures to the AISI Specification, Gregory J. Hancock et al., 2001

ASTM A29: Standard Specification for Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for

Carbon Steel Handbook, D. Gandy, 2007

ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015