AISI 416 Stainless Steel vs. AWS E410NiMo

Both AISI 416 stainless steel and AWS E410NiMo are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AISI 416 stainless steel and the bottom bar is AWS E410NiMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 13 to 31
17
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 510 to 800
850

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Melting Completion (Liquidus), °C 1530
1440
Melting Onset (Solidus), °C 1480
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
24
Thermal Expansion, µm/m-K 9.9
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
10
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 1.9
2.4
Embodied Energy, MJ/kg 27
34
Embodied Water, L/kg 100
110

Common Calculations

PREN (Pitting Resistance) 13
14
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18 to 29
30
Strength to Weight: Bending, points 18 to 25
26
Thermal Diffusivity, mm2/s 8.1
6.5
Thermal Shock Resistance, points 19 to 30
23

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.060
Chromium (Cr), % 12 to 14
11 to 12.5
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 83.2 to 87.9
79 to 84.6
Manganese (Mn), % 0 to 1.3
0 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.7
Nickel (Ni), % 0
4.0 to 5.0
Phosphorus (P), % 0 to 0.060
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.9
Sulfur (S), % 0.15 to 0.35
0 to 0.030