ASTM A182 Grade F23 vs. EN 1.4988 Stainless Steel

Both ASTM A182 grade F23 and EN 1.4988 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F23 and the bottom bar is EN 1.4988 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
34
Fatigue Strength, MPa 320
230
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 360
430
Tensile Strength: Ultimate (UTS), MPa 570
640
Tensile Strength: Yield (Proof), MPa 460
290

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 450
920
Melting Completion (Liquidus), °C 1500
1450
Melting Onset (Solidus), °C 1450
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
23
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 2.5
6.0
Embodied Energy, MJ/kg 36
89
Embodied Water, L/kg 59
150

Common Calculations

PREN (Pitting Resistance) 5.7
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
180
Resilience: Unit (Modulus of Resilience), kJ/m3 550
210
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 17
14

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Boron (B), % 0.0010 to 0.0060
0
Carbon (C), % 0.040 to 0.1
0.040 to 0.1
Chromium (Cr), % 1.9 to 2.6
15.5 to 17.5
Iron (Fe), % 93.2 to 96.2
62.1 to 69.5
Manganese (Mn), % 0.1 to 0.6
0 to 1.5
Molybdenum (Mo), % 0.050 to 0.3
1.1 to 1.5
Nickel (Ni), % 0 to 0.4
12.5 to 14.5
Niobium (Nb), % 0.020 to 0.080
0.4 to 1.2
Nitrogen (N), % 0 to 0.015
0.060 to 0.14
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0.3 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.0050 to 0.060
0
Tungsten (W), % 1.5 to 1.8
0
Vanadium (V), % 0.2 to 0.3
0.6 to 0.85