ASTM A182 Grade F3VCb vs. AWS E2594
Both ASTM A182 grade F3VCb and AWS E2594 are iron alloys. They have 64% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is AWS E2594.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 21 | |
| 17 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 74 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1440 |
| Melting Onset (Solidus), °C | 1430 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 40 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.5 | |
| 22 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 4.3 |
| Embodied Energy, MJ/kg | 33 | |
| 60 |
| Embodied Water, L/kg | 64 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 6.3 | |
| 43 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 24 | |
| 30 |
| Strength to Weight: Bending, points | 22 | |
| 25 |
| Thermal Diffusivity, mm2/s | 11 | |
| 4.3 |
| Thermal Shock Resistance, points | 19 | |
| 21 |
Alloy Composition
| Calcium (Ca), % | 0.00050 to 0.015 | |
| 0 |
| Carbon (C), % | 0.1 to 0.15 | |
| 0 to 0.040 |
| Chromium (Cr), % | 2.7 to 3.3 | |
| 24 to 27 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.75 |
| Iron (Fe), % | 93.8 to 95.8 | |
| 53.8 to 63.8 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0.5 to 2.0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 3.5 to 4.5 |
| Nickel (Ni), % | 0 to 0.25 | |
| 8.0 to 10.5 |
| Niobium (Nb), % | 0.015 to 0.070 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.015 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |