ASTM A182 Grade F3VCb vs. SAE-AISI O1 Steel

Both ASTM A182 grade F3VCb and SAE-AISI O1 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3VCb and the bottom bar is SAE-AISI O1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 670
640 to 2060

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
43
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
3.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.4
1.9
Embodied Energy, MJ/kg 33
27
Embodied Water, L/kg 64
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
23 to 73
Strength to Weight: Bending, points 22
21 to 46
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 19
21 to 68

Alloy Composition

Calcium (Ca), % 0.00050 to 0.015
0
Carbon (C), % 0.1 to 0.15
0.85 to 1.0
Chromium (Cr), % 2.7 to 3.3
0.4 to 0.6
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 93.8 to 95.8
95 to 97.4
Manganese (Mn), % 0.3 to 0.6
1.0 to 1.4
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.25
0 to 0.3
Niobium (Nb), % 0.015 to 0.070
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.015
0
Tungsten (W), % 0
0.4 to 0.6
Vanadium (V), % 0.2 to 0.3
0 to 0.3