ASTM A372 Grade J Steel vs. SAE-AISI 1021 Steel

Both ASTM A372 grade J steel and SAE-AISI 1021 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A372 grade J steel and the bottom bar is SAE-AISI 1021 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 310
130 to 150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 22
17 to 27
Fatigue Strength, MPa 310 to 570
190 to 300
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 410 to 630
310 to 320
Tensile Strength: Ultimate (UTS), MPa 650 to 1020
480 to 530
Tensile Strength: Yield (Proof), MPa 430 to 850
260 to 450

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 20
18
Embodied Water, L/kg 51
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 170
84 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 500 to 1930
180 to 530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 23 to 36
17 to 19
Strength to Weight: Bending, points 21 to 29
17 to 18
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 19 to 30
15 to 17

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.18 to 0.23
Chromium (Cr), % 0.8 to 1.2
0
Iron (Fe), % 96.7 to 97.8
98.8 to 99.22
Manganese (Mn), % 0.75 to 1.1
0.6 to 0.9
Molybdenum (Mo), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.010
0 to 0.050

Comparable Variants