ASTM Grade HE Steel vs. SAE-AISI 1021 Steel

Both ASTM grade HE steel and SAE-AISI 1021 steel are iron alloys. They have 61% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM grade HE steel and the bottom bar is SAE-AISI 1021 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
130 to 150
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 10
17 to 27
Fatigue Strength, MPa 160
190 to 300
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 670
480 to 530
Tensile Strength: Yield (Proof), MPa 310
260 to 450

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.5
1.4
Embodied Energy, MJ/kg 50
18
Embodied Water, L/kg 190
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
84 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 240
180 to 530
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
17 to 19
Strength to Weight: Bending, points 22
17 to 18
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 14
15 to 17

Alloy Composition

Carbon (C), % 0.2 to 0.5
0.18 to 0.23
Chromium (Cr), % 26 to 30
0
Iron (Fe), % 53.9 to 65.8
98.8 to 99.22
Manganese (Mn), % 0 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0 to 0.050