MakeItFrom.com
Menu (ESC)

AWS BAg-21 vs. AWS E80C-Ni3

AWS BAg-21 belongs to the otherwise unclassified metals classification, while AWS E80C-Ni3 belongs to the iron alloys. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS BAg-21 and the bottom bar is AWS E80C-Ni3.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 85
190
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
72
Tensile Strength: Ultimate (UTS), MPa 150
630

Thermal Properties

Latent Heat of Fusion, J/g 140
260
Melting Completion (Liquidus), °C 800
1450
Melting Onset (Solidus), °C 690
1410
Specific Heat Capacity, J/kg-K 280
470
Thermal Expansion, µm/m-K 19
13

Otherwise Unclassified Properties

Density, g/cm3 9.8
7.8
Embodied Energy, MJ/kg 970
23

Common Calculations

Stiffness to Weight: Axial, points 4.8
13
Stiffness to Weight: Bending, points 15
24
Strength to Weight: Axial, points 4.2
22
Strength to Weight: Bending, points 6.4
21
Thermal Shock Resistance, points 6.6
19

Alloy Composition

Carbon (C), % 0
0 to 0.12
Copper (Cu), % 27.5 to 29.5
0 to 0.35
Iron (Fe), % 0
92.8 to 97.3
Manganese (Mn), % 0
0 to 1.5
Nickel (Ni), % 2.0 to 3.0
2.8 to 3.8
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.9
Silver (Ag), % 62 to 64
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 5.0 to 7.0
0
Vanadium (V), % 0
0 to 0.030
Residuals, % 0 to 0.15
0 to 0.5