EN 1.0314 Steel vs. EN 1.0213 Steel

Both EN 1.0314 steel and EN 1.0213 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is EN 1.0213 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92 to 120
92 to 120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24 to 25
12 to 25
Fatigue Strength, MPa 140 to 220
160 to 240
Poisson's Ratio 0.29
0.29
Reduction in Area, % 78 to 86
72 to 80
Shear Modulus, GPa 73
73
Shear Strength, MPa 200 to 250
230 to 270
Tensile Strength: Ultimate (UTS), MPa 320 to 400
320 to 430
Tensile Strength: Yield (Proof), MPa 190 to 310
220 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
7.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68 to 87
33 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 95 to 250
120 to 300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11 to 14
11 to 15
Strength to Weight: Bending, points 13 to 15
13 to 16
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 10 to 13
10 to 14

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0.020 to 0.060
Carbon (C), % 0 to 0.030
0.060 to 0.1
Iron (Fe), % 99.365 to 99.78
99.245 to 99.67
Manganese (Mn), % 0.2 to 0.4
0.25 to 0.45
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 0.1
0 to 0.1
Sulfur (S), % 0 to 0.025
0 to 0.025

Comparable Variants