EN 1.0314 Steel vs. Grade 12 Titanium
EN 1.0314 steel belongs to the iron alloys classification, while grade 12 titanium belongs to the titanium alloys.
For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is grade 12 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 92 to 120 | |
| 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 24 to 25 | |
| 21 |
| Fatigue Strength, MPa | 140 to 220 | |
| 280 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Reduction in Area, % | 78 to 86 | |
| 28 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Shear Strength, MPa | 200 to 250 | |
| 330 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 400 | |
| 530 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 320 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1660 |
| Melting Onset (Solidus), °C | 1430 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 53 | |
| 21 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 6.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 37 |
| Density, g/cm3 | 7.9 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 31 |
| Embodied Energy, MJ/kg | 18 | |
| 500 |
| Embodied Water, L/kg | 46 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 87 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 250 | |
| 770 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 11 to 14 | |
| 32 |
| Strength to Weight: Bending, points | 13 to 15 | |
| 32 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.5 |
| Thermal Shock Resistance, points | 10 to 13 | |
| 37 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.080 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 99.365 to 99.78 | |
| 0 to 0.3 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0.2 to 0.4 |
| Nickel (Ni), % | 0 | |
| 0.6 to 0.9 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 97.6 to 99.2 |
| Residuals, % | 0 | |
| 0 to 0.4 |