EN 1.0503 Steel vs. EN 1.4821 Stainless Steel

Both EN 1.0503 steel and EN 1.4821 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0503 steel and the bottom bar is EN 1.4821 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16
18
Fatigue Strength, MPa 210
280
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 72
79
Shear Strength, MPa 380
450
Tensile Strength: Ultimate (UTS), MPa 630
730
Tensile Strength: Yield (Proof), MPa 310
450

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 48
17
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
15
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.4
2.9
Embodied Energy, MJ/kg 19
41
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83
110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
500
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 22
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 13
4.6
Thermal Shock Resistance, points 20
21

Alloy Composition

Carbon (C), % 0.42 to 0.5
0.1 to 0.2
Chromium (Cr), % 0 to 0.4
24.5 to 26.5
Iron (Fe), % 97.3 to 99.08
64.2 to 71.1
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
3.5 to 5.5
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.4
0.8 to 1.5
Sulfur (S), % 0 to 0.045
0 to 0.015