EN 1.1106 Steel vs. C95500 Bronze

EN 1.1106 steel belongs to the iron alloys classification, while C95500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is C95500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 24
8.4 to 10
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
44
Tensile Strength: Ultimate (UTS), MPa 550
700 to 850
Tensile Strength: Yield (Proof), MPa 370
320 to 470

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 400
230
Melting Completion (Liquidus), °C 1460
1050
Melting Onset (Solidus), °C 1420
1040
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 50
42
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
28
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.6
3.5
Embodied Energy, MJ/kg 22
57
Embodied Water, L/kg 50
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
58 to 61
Resilience: Unit (Modulus of Resilience), kJ/m3 360
420 to 950
Stiffness to Weight: Axial, points 13
8.0
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 19
24 to 29
Strength to Weight: Bending, points 19
21 to 24
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 17
24 to 29

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0.020 to 0.024
10 to 11.5
Carbon (C), % 0 to 0.18
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.3
78 to 84
Iron (Fe), % 96.2 to 98.9
3.0 to 5.0
Manganese (Mn), % 1.1 to 1.7
0 to 3.5
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.5
3.0 to 5.5
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.0050
0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.1
0
Residuals, % 0
0 to 0.5