EN 1.4003 Stainless Steel vs. C92500 Bronze

EN 1.4003 stainless steel belongs to the iron alloys classification, while C92500 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is C92500 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 22
11
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 540
310
Tensile Strength: Yield (Proof), MPa 320
190

Thermal Properties

Latent Heat of Fusion, J/g 270
190
Maximum Temperature: Mechanical, °C 720
170
Melting Completion (Liquidus), °C 1440
980
Melting Onset (Solidus), °C 1400
870
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 25
63
Thermal Expansion, µm/m-K 10
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
12
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
12

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
35
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 1.9
3.7
Embodied Energy, MJ/kg 27
61
Embodied Water, L/kg 97
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
30
Resilience: Unit (Modulus of Resilience), kJ/m3 260
170
Stiffness to Weight: Axial, points 14
6.8
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 19
9.8
Strength to Weight: Bending, points 19
12
Thermal Diffusivity, mm2/s 6.7
20
Thermal Shock Resistance, points 19
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 10.5 to 12.5
0
Copper (Cu), % 0
85 to 88
Iron (Fe), % 83.9 to 89.2
0 to 0.3
Lead (Pb), % 0
1.0 to 1.5
Manganese (Mn), % 0 to 1.5
0
Nickel (Ni), % 0.3 to 1.0
0.8 to 1.5
Nitrogen (N), % 0 to 0.030
0
Phosphorus (P), % 0 to 0.040
0 to 1.5
Silicon (Si), % 0 to 1.0
0 to 0.0050
Sulfur (S), % 0 to 0.015
0 to 0.050
Tin (Sn), % 0
10 to 12
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.7