MakeItFrom.com
Menu (ESC)

EN 1.4003 Stainless Steel vs. S24000 Stainless Steel

Both EN 1.4003 stainless steel and S24000 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 79% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4003 stainless steel and the bottom bar is S24000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
39
Fatigue Strength, MPa 210
370
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 340
530
Tensile Strength: Ultimate (UTS), MPa 540
770
Tensile Strength: Yield (Proof), MPa 320
430

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Maximum Temperature: Corrosion, °C 390
410
Maximum Temperature: Mechanical, °C 720
910
Melting Completion (Liquidus), °C 1440
1390
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 10
17

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.9
2.7
Embodied Energy, MJ/kg 27
39
Embodied Water, L/kg 97
150

Common Calculations

PREN (Pitting Resistance) 12
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
260
Resilience: Unit (Modulus of Resilience), kJ/m3 260
470
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
28
Strength to Weight: Bending, points 19
24
Thermal Shock Resistance, points 19
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 10.5 to 12.5
17 to 19
Iron (Fe), % 83.9 to 89.2
61.5 to 69
Manganese (Mn), % 0 to 1.5
11.5 to 14.5
Nickel (Ni), % 0.3 to 1.0
2.3 to 3.7
Nitrogen (N), % 0 to 0.030
0.2 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030