EN 1.4123 Stainless Steel vs. Grade VDSiCrV Steel

Both EN 1.4123 stainless steel and grade VDSiCrV steel are iron alloys. They have 83% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4123 stainless steel and the bottom bar is grade VDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 250
630
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
80
Tensile Strength: Ultimate (UTS), MPa 720 to 810
2100

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Mechanical, °C 840
420
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 23
47
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.8
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.3
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 4.2
1.9
Embodied Energy, MJ/kg 62
26
Embodied Water, L/kg 120
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26 to 29
75
Strength to Weight: Bending, points 23 to 25
47
Thermal Diffusivity, mm2/s 6.3
13
Thermal Shock Resistance, points 26 to 29
63

Alloy Composition

Carbon (C), % 0.35 to 0.5
0.5 to 0.7
Chromium (Cr), % 14 to 16.5
0.5 to 1.0
Copper (Cu), % 0
0 to 0.060
Iron (Fe), % 76.7 to 84.6
96.1 to 97.8
Manganese (Mn), % 0 to 1.0
0.4 to 0.9
Molybdenum (Mo), % 1.0 to 2.5
0
Nickel (Ni), % 0 to 0.5
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
1.2 to 1.7
Sulfur (S), % 0 to 0.030
0 to 0.020
Vanadium (V), % 0 to 1.5
0.1 to 0.25