MakeItFrom.com
Menu (ESC)

EN 1.4518 Stainless Steel vs. AISI 317L Stainless Steel

Both EN 1.4518 stainless steel and AISI 317L stainless steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is AISI 317L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
44
Fatigue Strength, MPa 160
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
82
Tensile Strength: Ultimate (UTS), MPa 490
550
Tensile Strength: Yield (Proof), MPa 210
250

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 1000
1010
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
21
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.0
4.3
Embodied Energy, MJ/kg 55
59
Embodied Water, L/kg 160
160

Common Calculations

PREN (Pitting Resistance) 30
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
200
Resilience: Unit (Modulus of Resilience), kJ/m3 100
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 4.1
3.8
Thermal Shock Resistance, points 14
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
18 to 20
Iron (Fe), % 61.4 to 70
58 to 68
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 3.0 to 3.5
3.0 to 4.0
Nickel (Ni), % 9.0 to 12
11 to 15
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030