EN 1.4518 Stainless Steel vs. EN 1.4590 Stainless Steel

Both EN 1.4518 stainless steel and EN 1.4590 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.4590 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
26
Fatigue Strength, MPa 160
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 490
480
Tensile Strength: Yield (Proof), MPa 210
270

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
470
Maximum Temperature: Mechanical, °C 1000
860
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
26
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
11
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.0
2.5
Embodied Energy, MJ/kg 55
37
Embodied Water, L/kg 160
120

Common Calculations

PREN (Pitting Resistance) 30
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 100
190
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
17
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 4.1
7.0
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 18 to 20
16 to 17.5
Iron (Fe), % 61.4 to 70
79.7 to 83.7
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
0
Niobium (Nb), % 0
0.35 to 0.55
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Zirconium (Zr), % 0
0 to 0.15