EN 1.4518 Stainless Steel vs. EN 1.4959 Stainless Steel

Both EN 1.4518 stainless steel and EN 1.4959 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is EN 1.4959 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
40
Fatigue Strength, MPa 160
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 490
630
Tensile Strength: Yield (Proof), MPa 210
190

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
510
Maximum Temperature: Mechanical, °C 1000
1090
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
12
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 20
31
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 4.0
5.4
Embodied Energy, MJ/kg 55
76
Embodied Water, L/kg 160
200

Common Calculations

PREN (Pitting Resistance) 30
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
190
Resilience: Unit (Modulus of Resilience), kJ/m3 100
96
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.1
3.2
Thermal Shock Resistance, points 14
15

Alloy Composition

Aluminum (Al), % 0
0.25 to 0.65
Carbon (C), % 0 to 0.030
0.050 to 0.1
Chromium (Cr), % 18 to 20
19 to 22
Cobalt (Co), % 0
0 to 0.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 61.4 to 70
39.4 to 50.5
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 3.0 to 3.5
0
Nickel (Ni), % 9.0 to 12
30 to 34
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.5
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.25 to 0.65