EN 1.4525 Stainless Steel vs. SAE-AISI 1144 Steel

Both EN 1.4525 stainless steel and SAE-AISI 1144 steel are iron alloys. They have 75% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4525 stainless steel and the bottom bar is SAE-AISI 1144 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 5.6 to 13
11 to 17
Fatigue Strength, MPa 480 to 540
280 to 430
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 1030 to 1250
750 to 840
Tensile Strength: Yield (Proof), MPa 840 to 1120
420 to 690

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 860
400
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 18
51
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 13
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.8
1.4
Embodied Energy, MJ/kg 39
19
Embodied Water, L/kg 130
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68 to 130
91 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 1820 to 3230
480 to 1290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 36 to 45
27 to 30
Strength to Weight: Bending, points 29 to 33
23 to 25
Thermal Diffusivity, mm2/s 4.7
14
Thermal Shock Resistance, points 34 to 41
22 to 24

Alloy Composition

Carbon (C), % 0 to 0.070
0.4 to 0.48
Chromium (Cr), % 15 to 17
0
Copper (Cu), % 2.5 to 4.0
0
Iron (Fe), % 70.4 to 79
97.5 to 98
Manganese (Mn), % 0 to 1.0
1.4 to 1.7
Molybdenum (Mo), % 0 to 0.8
0
Nickel (Ni), % 3.5 to 5.5
0
Niobium (Nb), % 0 to 0.35
0
Nitrogen (N), % 0 to 0.050
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.8
0
Sulfur (S), % 0 to 0.025
0.24 to 0.33

Comparable Variants