EN 1.4886 Stainless Steel vs. R60704 Alloy

EN 1.4886 stainless steel belongs to the iron alloys classification, while R60704 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.4886 stainless steel and the bottom bar is R60704 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
97
Elongation at Break, % 45
16
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
36
Tensile Strength: Ultimate (UTS), MPa 580
470
Tensile Strength: Yield (Proof), MPa 300
270

Thermal Properties

Latent Heat of Fusion, J/g 320
240
Specific Heat Capacity, J/kg-K 480
270
Thermal Conductivity, W/m-K 12
22
Thermal Expansion, µm/m-K 15
6.0

Otherwise Unclassified Properties

Density, g/cm3 8.0
6.7
Embodied Water, L/kg 190
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
64
Resilience: Unit (Modulus of Resilience), kJ/m3 230
370
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 20
20
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 3.1
12
Thermal Shock Resistance, points 14
58

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.050
Chromium (Cr), % 17 to 20
0.2 to 0.4
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 38.7 to 49
0.2 to 0.4
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 33 to 37
0
Nitrogen (N), % 0 to 0.1
0 to 0.025
Oxygen (O), % 0
0 to 0.18
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 1.0 to 2.0
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
1.0 to 2.0
Zirconium (Zr), % 0
93 to 98.8