EN 1.7231 Steel vs. EN 1.4828 Stainless Steel

Both EN 1.7231 steel and EN 1.4828 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is EN 1.4828 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240 to 280
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 12
33
Fatigue Strength, MPa 360 to 500
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 790 to 930
650
Tensile Strength: Yield (Proof), MPa 570 to 800
260

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
1000
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 46
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 20
48
Embodied Water, L/kg 51
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
170
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 28 to 33
23
Strength to Weight: Bending, points 24 to 27
22
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 23 to 27
14

Alloy Composition

Carbon (C), % 0.38 to 0.45
0 to 0.2
Chromium (Cr), % 0.8 to 1.2
19 to 21
Iron (Fe), % 96.4 to 98.1
61.1 to 68.5
Manganese (Mn), % 0.6 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
11 to 13
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.6
1.5 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.015