EN 1.7231 Steel vs. S24000 Stainless Steel

Both EN 1.7231 steel and S24000 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is S24000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240 to 280
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 12
39
Fatigue Strength, MPa 360 to 500
370
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 790 to 930
770
Tensile Strength: Yield (Proof), MPa 570 to 800
430

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 420
910
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
17

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.5
2.7
Embodied Energy, MJ/kg 20
39
Embodied Water, L/kg 51
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
260
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
470
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 28 to 33
28
Strength to Weight: Bending, points 24 to 27
24
Thermal Shock Resistance, points 23 to 27
16

Alloy Composition

Carbon (C), % 0.38 to 0.45
0 to 0.080
Chromium (Cr), % 0.8 to 1.2
17 to 19
Iron (Fe), % 96.4 to 98.1
61.5 to 69
Manganese (Mn), % 0.6 to 1.0
11.5 to 14.5
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
2.3 to 3.7
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0 to 0.025
0 to 0.060
Silicon (Si), % 0 to 0.6
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030