C94900 Bronze vs. AWS E90C-B9
C94900 bronze belongs to the copper alloys classification, while AWS E90C-B9 belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C94900 bronze and the bottom bar is AWS E90C-B9.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 17 | |
| 18 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 41 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 300 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 270 |
| Melting Completion (Liquidus), °C | 980 | |
| 1460 |
| Melting Onset (Solidus), °C | 910 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 470 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 14 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 7.0 |
| Density, g/cm3 | 8.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 55 | |
| 37 |
| Embodied Water, L/kg | 350 | |
| 91 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 | |
| 550 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 9.4 | |
| 25 |
| Strength to Weight: Bending, points | 11 | |
| 23 |
| Thermal Shock Resistance, points | 11 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0050 | |
| 0 to 0.040 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.080 to 0.13 |
| Chromium (Cr), % | 0 | |
| 8.0 to 10.5 |
| Copper (Cu), % | 79 to 81 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.3 | |
| 84.4 to 90.9 |
| Lead (Pb), % | 4.0 to 6.0 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 1.2 |
| Molybdenum (Mo), % | 0 | |
| 0.85 to 1.2 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 0 to 0.8 |
| Niobium (Nb), % | 0 | |
| 0.020 to 0.1 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.080 | |
| 0 to 0.015 |
| Tin (Sn), % | 4.0 to 6.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.3 |
| Zinc (Zn), % | 4.0 to 6.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |