N08135 Stainless Steel vs. AISI 416 Stainless Steel

Both N08135 stainless steel and AISI 416 stainless steel are iron alloys. They have 50% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is AISI 416 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
13 to 31
Fatigue Strength, MPa 220
230 to 340
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 400
340 to 480
Tensile Strength: Ultimate (UTS), MPa 570
510 to 800
Tensile Strength: Yield (Proof), MPa 240
290 to 600

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 430
390
Maximum Temperature: Mechanical, °C 1100
680
Melting Completion (Liquidus), °C 1440
1530
Melting Onset (Solidus), °C 1390
1480
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
9.9

Otherwise Unclassified Properties

Base Metal Price, % relative 39
7.0
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
1.9
Embodied Energy, MJ/kg 94
27
Embodied Water, L/kg 220
100

Common Calculations

PREN (Pitting Resistance) 38
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
98 to 140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
220 to 940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
18 to 29
Strength to Weight: Bending, points 19
18 to 25
Thermal Shock Resistance, points 13
19 to 30

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 20.5 to 23.5
12 to 14
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
83.2 to 87.9
Manganese (Mn), % 0 to 1.0
0 to 1.3
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.060
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0.15 to 0.35
Tungsten (W), % 0.2 to 0.8
0