N08135 Stainless Steel vs. EN 1.0108 Steel

Both N08135 stainless steel and EN 1.0108 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.0108 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
29
Fatigue Strength, MPa 220
150
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
250
Tensile Strength: Ultimate (UTS), MPa 570
380
Tensile Strength: Yield (Proof), MPa 240
200

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.1
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.5
Embodied Energy, MJ/kg 94
19
Embodied Water, L/kg 220
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
94
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
13
Strength to Weight: Bending, points 19
15
Thermal Shock Resistance, points 13
12

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.2
Carbon (C), % 0 to 0.030
0 to 0.13
Chromium (Cr), % 20.5 to 23.5
0 to 0.3
Copper (Cu), % 0 to 0.7
0 to 0.3
Iron (Fe), % 30.2 to 42.3
97.5 to 99.98
Manganese (Mn), % 0 to 1.0
0 to 0.7
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.080
Nickel (Ni), % 33 to 38
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.040
Tungsten (W), % 0.2 to 0.8
0
Vanadium (V), % 0
0 to 0.020